HONYEPO®G10/fr4 Epoxy Fiber Glass sheet combines a woven glass fabric and an epoxy resin laminate (tg approximately 130-c) that contains bromine. G10 provides consistent quality and good electrical properties under dry and humid conditions, as well as high flexural, impact, and bond strength at room temperatures. This product is suitable for a variety of structural, high humidity, and electrical insulation applications, which include terminal boards, lapping carriers, and disc and microelectronics polishing. Np510a complies with the requirements of mil-i-24768/27, type GF.

HONYEPO®G10 / fr4 Epoxy Fiber Glass sheet feature :
Higher mechanical properties.
Good mechanical workability.
Good heat resistance and moisture resistance.
In high temperature electric performance is stable.
Higher mechanical properties and dielectric properties.
In the middle temperature with high mechanical properties.
The flame retardant grade is UL94 V0
F grade Heat resistance and heat resistance (120 min) reaches to 180 ℃
High mechanical performances (bending, compression and stretching of transverse strength is above 330Mpa)
High dielectric properties of th e oil (25 ℃ in the vertical dielectric strength of 16 kv/mm)
HONYEPO®G10 / fr4 Epoxy Fiber Glass sheet application :
Motors and electrical equipment insulation parts
General machines parts and gear, generators, Pads, base, baffle,Generator, transformer, fixture, inverter, motor
Backing boards: PCB drilling machine, Plastic Mould, Injection Mould, Injection molding machine, Table grinding machine, ICT governance
Reinforcement sheets: Testing fixture PFC,FPC
Less than 3 mm is used for Raw materials of PCB flexible circuit board test processing
Needle plate, carrier board and insulating electrical and electronic products
G10 and FR4 glass cloth reinforced epoxy natural is typically a yellowish to light green color. The most versatile all-around laminate grades are continuous glass woven fabric impregnated with an epoxy resin binder. Epoxy resins are among the most versatile and widely used plastics in the electronics field, primarily because water absorption is virtually nil, rendering it an outstanding insulator.
Beyond its electrical insulating properties, epoxy resins exhibit great dimensional stability (shrinkage is usually less than 1 percent) and superior adhesive properties. G10/FR4 has extremely high mechanical strength, good dielectric loss properties, and good electric strength properties, both wet and dry.
The main difference between NEMA Grades G10 and FR4 is that FR4 is a fire retardant grade of G10. Therefore, FR4 can be safely substituted where G10 is called for, while G10 can never be substituted where FR4 is called for. G10 meets MIL-I-24768/2 GEE and FR4 meets MIL-I-24768/27 GEE-F.
G9 has good mechanical properties plus high resistance to flame, heat, arcing, and most strong alkali solutions. It is recommended for use where good mechanical properties are needed under wet conditions. Specification: MIL-1-24768/1, Type GME .
HONY plastic also CNC to your CAD drawing, cut to size to +-.005 tolerance, and sell full sheets in quantity. This G10 and FR4 material is also available thinner and thicker as well as in rod and tube. Please call our sales department for information.